Regularities in the structure and properties formation of aluminum-based composites during hot pressing S. Vorozhtsov, M. Khmeleva, A. Khrustalyov [et.al.]
Material type:
ArticleSubject(s): композиционные материалы на основе алюминия | горячее прессование | фазовый состав | кристаллическая структураGenre/Form: статьи в журналах Online resources: Click here to access online
In:
AIP Conference Proceedings Vol. 1772. P. 030017-1-030017-4Abstract: The purpose of this study is to investigate the phase composition, parameters of fine crystalline structure and mechanical properties of aluminum-based composites, produced by hot pressing with different synthesis temperatures and isothermal times. For synthesis of composites we used powder mixture of aluminum (particles size 700 nm) and carbon powder in a form of nanodiamonds (size 4 nm). It has been shown that after hot press processing a nanophase (crystallites size 25 nm) of aluminum carbide was formed. Regardless of the synthesis temperature for the maximum holding time of powder mixtures, the density of hot-pressed compacts is about 2.2-2.37 g/cm3. In particular, the value of bending strength of composite samples with a density of 2.37 g/cm3 ranges from 350 to 480 MPa. In the nonporous state, the bending strength of the composites may reach 920 MPa.
Библиогр.: 9 назв.
The purpose of this study is to investigate the phase composition, parameters of fine crystalline structure and mechanical properties of aluminum-based composites, produced by hot pressing with different synthesis temperatures and isothermal times. For synthesis of composites we used powder mixture of aluminum (particles size 700 nm) and carbon powder in a form of nanodiamonds (size 4 nm). It has been shown that after hot press processing a nanophase (crystallites size 25 nm) of aluminum carbide was formed. Regardless of the synthesis temperature for the maximum holding time of powder mixtures, the density of hot-pressed compacts is about 2.2-2.37 g/cm3. In particular, the value of bending strength of composite samples with a density of 2.37 g/cm3 ranges from 350 to 480 MPa. In the nonporous state, the bending strength of the composites may reach 920 MPa.
There are no comments on this title.