TY  - GEN
AU  - Буяков,Алесь Сергеевич
AU  - Васильева,Елизавета Олеговна
AU  - Ткачев,Дмитрий Александрович
TI  - Влияние микроструктуры и фазового состава на механические свойства композита ZrO2-MgO с бимодальной поровой структурой
KW  - оксид магния
KW  - диоксид циркония
KW  - спекание
KW  - рентгеноструктурный анализ
KW  - пределы прочности
KW  - керамика
KW  - экспериментальные данные
KW  - пористые керамические материалы
KW  - статьи в сборниках
N1  - Библиогр.: 5 назв
N2  - In this paper porous ceramics based on the Zr02-Mg0 system were studied. It was shown, that the addition of an organic pore-forming particles make it possible to obtain a bimodal pore structure. X-ray diffraction analysis showed that with the increasing of MgO concentration, the average size of Zr02 and MgO crystallites grows up and their crystal lattice microdistortion decrease. Strength with increasing of MgO concentration is increasing and the dependence of compressive strength from microstresses was found
UR  - http://vital.lib.tsu.ru/vital/access/manager/Repository/vtls:000636360
ER  -